Hydrolyzable nylon PA66 PA6, reinforced with 10% -50% fibers, can be customized
- Type: KLD6030W
- Product Name: Hydrolyzable nylon PA66 PA6, reinforced with 10% -50% fibers, can be customized
Through hot wire, needle flame, and ball pressure testing.
Fiber reinforced 5% - 60% customizable.
Product Details:
Product features: hydrolysis resistance, heat resistance, high strength, widely used in the automotive industry, electronics and electrical, electric tools, household appliances, industrial machinery, sports equipment and other fields.
| Typical physical properties | Type： | KLD6030W | |||
| Project | Condition | Value | Unit | Test method | |
| Physical Property | Melt Finger (MFR) | 220℃/2.16Kg | 4.02 | g/10 min | ASTM D1238 |
| Density | 23℃ | 1.33 | g/cm³ | ASTM D792 | |
| Mechanical Performance | Bending modulus | 1060 | kg/cm² | ASTM D638 | |
| Tensile strength | 11.4 | kg-cm/cm | ASTM D256 | ||
| Bending strength | 1670 | kg/cm² | ASTM D790 | ||
| Thermal performance | Hot deformation temperature | 1.80MPA | 205 | °C | ISO 75 |
| Melting point | 220 | °C | ISO 75 | ||
| Flame retardant performance | Flame retardant level | HB | NO | UL 94 | |
| Injection molding process | Drying temperature | 100-120 | °C | ||
| Drying time | 4-6 | hr | |||
| Forming temperature | 230-260 (±10-20) | °C | |||
| Mold temperature | 80-120 | °C | |||
| Material status: | Normal circulation | ||||
| Characteristic: | Hydrolysis resistance, heat resistance, high strength | ||||
| Purpose: | Automotive industry, electronics and electrical, electric tools, household appliances, industrial machinery, sports equipment, etc | ||||
| Processing method: | Injection molding | ||||
| Additives: | Fiber reinforced, 5-60% customizable | ||||
| Form: | Granules | ||||
| Source of physical parameters: | Non national third-party testing certification submitted by manufacturers for inspection | ||||
More Products:
Nitrogen based flame retardant nylon PA66 PA6, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6006V0
Nitrogen based flame retardant nylon PA66, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6600V0
Red phosphorus flame retardant nylon PA66, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6606V0
Reinforced flame-retardant nylon PA66 PA6, fiber reinforced 10% -50% can be customized
Type: KLD6030V0
Reinforced flame-retardant nylon PA66 PA6, fiber reinforced 10% -50% can be customized
Type: KLD6630V0
Fiberglass reinforced nylon PA66GF PA6GF, can be customized with 10% -50% fiber reinforcement
Type: KLD6030G
Fiberglass reinforced nylon PA66GF PA6GF, can be customized with 10% -50% fiber reinforcement
Type: KLD6630G
Reinforced and toughened nylon PA66 PA6, customizable with 10% -50% fiber reinforcement
Type: KLD6030GT