Conductive nylon PA66 PA6, reinforced with 10% -50% fibers, can be customized
- Type: KLD6030CF
- Product Name: Conductive nylon PA66 PA6, reinforced with 10% -50% fibers, can be customized
Through hot wire, needle flame, and ball pressure testing.
Fiber reinforced 5% - 60% customizable.
Product Details:
Product features: Carbon fiber reinforced, conductive, anti-static, carbon fiber reinforced, widely used in the automotive industry, electronics and electrical, electric tools, household appliances, industrial machinery, sports equipment and other fields.
| Typical physical properties | Type： | KLD6030CF | |||
| Project | Condition | Value | Unit | Test method | |
| Physical Property | Melt Finger (MFR) | 220℃-5kg | 12 | g/10 min | GB/T 3682-2000 |
| density | 1.21 | g/cm³ | GB 1033-1986 | ||
| Mechanical Performance | Tensile yield strength | 40.8 | MPa | GB/T 1040.2-2006 | |
| Bending modulus | 2210 | MPa | GB/T 9341-2000 | ||
| tensile strength | 40.9 | MPa | GB/T 1040-1992 | ||
| Impact strength of cantilever beam notch | 21 | kJ/m² | GB/T 1843-2000 | ||
| elongation at break | 12.25 | % | GB/T 1040-1992 | ||
| Notched impact strength of simply supported beams | 157 | kJ/m² | GB/T 1043.1-2008 | ||
| bending strength | 2mm/min | 54.3 | MPa | GB/T 9341-2000 | |
| Charpy Notched Impact Strength | 16 | kJ/m² | GB/T 1043.1-2008 | ||
| Thermal performance | Hot deformation temperature | 1.80MPA | 205 | °C | ISO 75 |
| Melting point | 220 | °C | ISO 75 | ||
| Electrical performance | Surface resistivity | 10^5 | ohms | ASTM D257 | |
| Flame retardant performance | Flame retardant level | UL-94 | V-2 | GB/T 2408-1996 | |
| Injection molding process | Drying temperature | 100-120 | °C | ||
| Drying time | 4-6 | hr | |||
| Forming temperature | 230-260 (±10-20) | °C | |||
| Mold temperature | 80-120 | °C | |||
| Material status: | Normal circulation | ||||
| Characteristic: | Conductive, anti-static | ||||
| Purpose: | Automotive industry, electronics and electrical, electric tools, household appliances, industrial machinery, sports equipment, etc | ||||
| Processing method: | Injection molding | ||||
| Additives: | Fiber reinforced, 5-60% customizable | ||||
| Form: | Granules | ||||
| Source of physical parameters: | Non national third-party testing certification submitted by manufacturers for inspection | ||||
More Products:
Nitrogen based flame retardant nylon PA66 PA6, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6006V0
Nitrogen based flame retardant nylon PA66, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6600V0
Red phosphorus flame retardant nylon PA66, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6606V0
Reinforced flame-retardant nylon PA66 PA6, fiber reinforced 10% -50% can be customized
Type: KLD6030V0
Reinforced flame-retardant nylon PA66 PA6, fiber reinforced 10% -50% can be customized
Type: KLD6630V0
Fiberglass reinforced nylon PA66GF PA6GF, can be customized with 10% -50% fiber reinforcement
Type: KLD6030G
Fiberglass reinforced nylon PA66GF PA6GF, can be customized with 10% -50% fiber reinforcement
Type: KLD6630G
Reinforced and toughened nylon PA66 PA6, customizable with 10% -50% fiber reinforcement
Type: KLD6030GT