UV resistant, anti-aging nylon PA66 PA6, fiber reinforced 10% -50% can be customized
- Type: KLD6030UV
- Product Name: UV resistant, anti-aging nylon PA66 PA6, fiber reinforced 10% -50% can be customized
Through hot wire, needle flame, and ball pressure testing.
Fiber reinforced 5% - 60% customizable.
Product Details:
Product features: Heat resistance, aging resistance, high flow, good film removal performance, widely used in the automotive industry, electronics and electrical, electric tools, household appliances, industrial machinery, sports equipment and other fields.
| Typical physical properties | Type： | KLD6030UV | |||
| Project | Condition | Value | Unit | Test method | |
| Physical Property | Melt Finger (MVR) | 275 °C - 5,0 kg | 45 | cm³/10min | ISO 1133 |
| Density | 1.36 | g/cm³ | ISO 1183 | ||
| Shrinkage rate | Flow rate: 23 ° C, 72 hours | 0.30-0.50 | % | ISO 2577 | |
| Shrinkage rate | Lateral flow rate: 23 ° C, 72 hours | 0.80-1.00 | % | ISO 2577 | |
| Mechanical Performance | Tensile modulus | 9500 | MPa | ISO 527-2,-1 | |
| Notched impact strength of cantilever beam | Dry, 23 ° C | 80 | kJ/m² | ISO 180/1U | |
| Bending modulus | 8500 | MPa | ISO 178 | ||
| Tensile fracture strength | 180 | MPa | ISO 527-2/5 | ||
| Impact strength of cantilever beam notch | 23°C | 15 | kJ/m² | ISO 180/1A | |
| elongation at break | 3.5 | % | ISO 527-2/5 | ||
| Notched impact strength of simply supported beams | 23°C | 90 | kJ/m² | ISO 179/1eU | |
| bending strength | 270 | MPa | ISO 178 | ||
| Charpy Notched Impact Strength | 23°C | 15 | kJ/m² | ISO 179/1eA | |
| Thermal performance | Hot deformation temperature | 1.8 MPa, unannealed | 205 | °C | ISO 75-2/A |
| melting point | dry | 220 | °C | ISO 11357-3 | |
| Electrical performance | Surface resistivity | 10000000000000 | ohms | IEC 60093 | |
| Leakage trace index | Drying, Solution A | 500 | V | IEC 60112 | |
| Volume resistivity | 1000000000000000 | ohms·cm | IEC 60093 | ||
| Flame retardant performance | Flame retardant level | 0.8 mm | HB | no | UL 94 |
| Glowing wire flammability index | 1.00 to 3.00 mm | 650 | °C | IEC 60695-2-12 | |
| Burning rate | <100 | mm/min | FMVSS 302 | ||
| Injection molding process | Drying temperature | 100-120 | °C | ||
| Drying time | 4-6 | hr | |||
| Forming temperature | 230-260 (±10-20) | °C | |||
| Mold temperature | 80-120 | °C | |||
| Material status: | Normal circulation | ||||
| Characteristic: | Heat resistance, aging resistance, high flow | ||||
| Purpose: | Automotive industry, electronics and electrical, electric tools, household appliances, industrial machinery, sports equipment, etc | ||||
| Processing method: | Injection molding | ||||
| Additives: | Fiber reinforced, 5-60% customizable | ||||
| Form: | Granules | ||||
| Source of physical parameters: | Non national third-party testing certification submitted by manufacturers for inspection | ||||
More Products:
Nitrogen based flame retardant nylon PA66 PA6, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6006V0
Nitrogen based flame retardant nylon PA66, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6600V0
Red phosphorus flame retardant nylon PA66, tested by hot wire, needle flame, and ball pressure testing. Fiber reinforced 5%-60% customizable.
Type: KLD6606V0
Reinforced flame-retardant nylon PA66 PA6, fiber reinforced 10% -50% can be customized
Type: KLD6030V0
Reinforced flame-retardant nylon PA66 PA6, fiber reinforced 10% -50% can be customized
Type: KLD6630V0
Fiberglass reinforced nylon PA66GF PA6GF, can be customized with 10% -50% fiber reinforcement
Type: KLD6030G
Fiberglass reinforced nylon PA66GF PA6GF, can be customized with 10% -50% fiber reinforcement
Type: KLD6630G
Reinforced and toughened nylon PA66 PA6, customizable with 10% -50% fiber reinforcement
Type: KLD6030GT